Nickel improves glass-forming ability of mischmetal substituted yttrium in the Mg–Cu based alloys

Abstract The substitution of Y by mischmetal was investigated on the Mg 65 Cu 25 Y 10 metallic glass, in order to reduce pure rare earth content and improve manufacturing for potential applications. Works showed that this substitution is well accommodated by partial substitution of Cu by Ni. Alloys were prepared by planar flow melt spinning, with various amounts of mischmetal (0, 5 or 10 at.%) and Ni (0, 5, 12.5, 20 or 25 at.%). With increasing content of mischmetal and nickel, the glass forming ability, especially the width of the supercooled liquid region tends to decrease. However, an optimal substitution of Cu by Ni (12.5 at.%) in an alloy free from Y has been identified to present an appreciable glass forming ability with a supercooled liquid region of 35 K.