The influences of cations on the properties of Y–Mg–Si–Al–O–N glasses

Abstract Two series (A and B series) of oxynitride glasses were prepared by melting batches at 1580 °C for 3 h under local CO reducing atmosphere in a Si–Mo-heated resistance furnace. Nominal compositions of A and B series glasses in equivalent percent (eq.%) are (28−x)Y:xMg:48Si:24Al:83O:17N and (28−x)Y:xMg:56Si:16Al:83O:17N (x = 0, 7, 14, 21), respectively. The influences of Mg/Y and Al/Si ratios on the properties such as glass transition temperature (Tg), crystallization temperature (TC), knoop hardness (H), three-point bending strength (σ) and chemical durability in 20%HF were investigated. At the same time, the relationship between these properties and the structures of the glasses were discussed. At constant ratio Si–Al–O–N, Tg decreases nonlinearly but glass leaching ratio increases linearly with increasing Mg/Y ratio. However, H and σ increase first and then decrease as the Mg/Y ratio increases. When the Y/Mg/O/N ratio is constant, Tg decreases slightly but H and σ increase slightly as the Al/Si ratio increases.