Synthesis and characterization of ternary glasses in the system Na2Se-Ga2Se3-GeSe2

Abstract Chalcogenide glasses in the system Na2Se-Ga2Se3-GeSe2 (NGGS) have been synthesized and characterized using Raman spectroscopy as well as density and glass transition temperature measurements. Results are compared to those from the analogous system BaSe-Ga2Se3-GeSe2 (BGGS) in an attempt to shed light on the comparative roles of Na and Ba as modifying elements in chalcogenide networks. In general, both NGGS and BGGS glasses exhibit the corner-sharing network of (Ga/Ge)Se4 tetrahedra that is characteristic of glasses containing Ga–Ge–Se. Some amount of tetrahedral edge-sharing and Ge–Ge bonding exists, but the concentration of Ge–Ge bonds in the network is heavily dependent on both the ratio R = Na2Se(BaSe)/Ga2Se3 and the type of the modifying element. The addition of Na2Se to an NGGS glass with R 1 indicating that Na2Se is a much more efficient modifier that lowers the connectivity of the Ga–Ge–Se tetrahedral network via the formation of non-bridging Se atoms.