Influence of maghemite concentration on magnetic interactions in maghemite/PTT-block-PTMO nanocomposite

Abstract Temperature dependence of dc magnetization and ferromagnetic resonance (FMR) of two samples containing γ-Fe 2 O 3 (maghemite) magnetic nanoparticles dispersed at low concentration (0.1 and 0.3 wt%) in a nanocomposite based on a poly(ether–ester) multiblock copolymer (PTT-block-PTMO) matrix was investigated. The polymer filler was in a powder form consisting of small-sized magnetic nanoparticles arranged in agglomerates 2–3 μm long and 100 nm thick. The studied samples were characterized by SEM spectroscopy. The SEM showed that the concentration of magnetic nanoparticles was homogenous in both samples The temperature dependence of the dc magnetization revealed that the blocking was about 100 K and the ZFC (zero-field cooling) mode at low magnetic fields uncovered the presence of magnetic interactions between magnetic nanoparticles depending on the properties of the matrix. FMR measurements were carried out in the temperature range 4.2–300 K. An intense resonance absorption line attributed to γ-Fe 2 O 3 nanoparticles was recorded with a slightly asymmetric lineshape. At room temperature the resonance line was centered at H r = 3241(2) and 3253(2) G, with linewidths of Δ H = 1069(1) and 1070(1) G for samples with concentrations of 0.1 and 0.3 wt%, respectively. All FMR parameters showed an anomalous behavior at matrix critical temperatures. It was shown that the difference in concentration of magnetic nanoparticles could be responsible for the observed differences in the thermal behavior of the FMR spectra.