Effect of crystallization behavior on the oxidation resistance of a Zr–Al–Cu metallic glass below the crystallization temperature

Abstract The crystallization behavior of Zr 65.0 Al 7.5 Cu 27.5 (at.%) metallic glass with 753 and 1053 K annealing treatment and its effect on oxidation resistance around the supercooled liquid region at 623 and 663 K was studied. The crystalline phase of bct-Zr 2 Cu precipitates for the specimen annealed at 753 K was observed, while duplex structures of bct-Zr 2 Cu and Zr 2 Al formed in the specimen annealed at 1053 K. The oxidation resistance of the specimen depended on the amount of crystalline precipitates. Regardless of the exposure temperature, the annealed specimens showed higher oxidation resistance than the melt-spun one, especially for the specimen annealed at 1053 K. The formation of numerous crystalline phases of bct-Zr 2 Cu and Zr 2 Al from the matrix was responsible for improving the oxidation resistance due to their higher oxidation resistance and promotion of the development of Al 2 O 3 and oxides of copper. The oxide constituents of the amorphous alloy after long exposure depended on the temperature. The oxide was composed of a large amount of CuO, some tetragonal and monoclinic-ZrO 2 and a minor amount of Cu 2 O as well as a slight amount of Al 2 O 3 for the melt-spun specimen during exposure at 623 K. Under the 663 K exposure, however, the oxide state of Cu 3+ in the scale was also detected.