Preparation and characterization of borosilicate glass-ceramics containing zirconolite and titanite crystalline phases

Lang Wu, Yuxiang Li, Yuancheng Teng, Guolong Meng

Publisher page

Abstract

Abstract CaCO 3 , ZrSiO 4 , and TiO 2 (abbreviated as CZST) in the stoichiometric mole ratio (2:1:3) were added to borosilicate system. Borosilicate glass-ceramics containing zirconolite and titanite crystalline phases were prepared by controlled crystallization of the parent glass. The effects of CZST addition (10, 20, 30, and 40 wt. %) on crystalline phases, microstructure, and chemical durability of the glass-ceramics were mainly investigated. The results show that the samples possess the amorphous structure when the concentration of CZST is lower than 30 wt. %. For the glass-ceramics with 30 wt. % CZST (GC-30) heated at 740 °C for 2 h, only the zirconolite-2M phase was observed. For the sample with 40 wt. % CZST (GC-40) heated at 810 °C for 2 h, the major crystalline phases are CaZrTi 2 O 7 and CaTiSiO 5 . In addition, the grains of the CaZrTi 2 O 7 and CaTiSiO 5 show a dendritic and columnar shape, respectively. The static leaching test shows that the normalized mass loss (NL i ) for B, Si, and Na of the sample GC-30 remains almost unchanged (~ 10 − 3 g/m 2 ) after 14 days. Compared to the borosilicate glass, the GC-30 possesses particularly the lower values of the NL i for B and Na. These results indicate that the borosilicate glass-ceramics containing zirconolite and/or titanite crystalline phases have the potential as host materials for actinide-rich high level radioactive wastes.
Source: openaire · Quality: candidate unverified · Source record ↗

Research context

OpenAlex topics: Nuclear materials and radiation effects · Nuclear Materials and Properties · Luminescence Properties of Advanced Materials

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

References (19)

Show source-provided references
1. Donald · J. Mater. Sci. · 1997 · 32 · 585110.1023/A:1018646507438 ↗
2. Caurant · J. Nucl. Mater. · 2006 · 354 · 14310.1016/j.jnucmat.2006.03.014 ↗
3. Gary Eller · Radiochim. Acta · 1985 · 39 · 1710.1524/ract.1985.39.1.17 ↗
4. He · J. Nucl. Mater. · 2008 · 376 · 20110.1016/j.jnucmat.2008.01.027 ↗
5. Taurines · J. Non-Cryst. Solids · 2011 · 357 · 272310.1016/j.jnoncrysol.2011.02.024 ↗
6. Zhang · J. Nucl. Mater. · 2013 · 432 · 54510.1016/j.jnucmat.2012.08.035 ↗
7. Loiseau · J. Nucl. Mater. · 2004 · 335 · 1410.1016/j.jnucmat.2004.05.020 ↗
8. Loiseau · J. Nucl. Mater. · 2010 · 402 · 3810.1016/j.jnucmat.2010.04.021 ↗
9. Fillet · 1997 · 531
10. Loiseau · J. Mater. Sci. · 2003 · 38 · 84310.1023/A:1021873301498 ↗
11. Rossell · Nature · 1980 · 283 · 28210.1038/283282a0 ↗
12. Hayward · 1988 · 427
13. Mahmoudysepehr · J. Am. Ceram. Soc. · 2009 · 92 · 154010.1111/j.1551-2916.2009.03095.x ↗
14. Y. C. Teng, S. G. Zhou, C. X. Che, Chinese Patent ZL200510021423.2 (2008).
15. Luo · J. Nucl. Mater. · 2001 · 298 · 18010.1016/S0022-3115(01)00592-X ↗
16. Martin · J. Nucl. Mater. · 2007 · 366 · 27710.1016/j.jnucmat.2007.02.002 ↗
17. Loiseau · J. Mater. Sci. · 2003 · 38 · 85310.1023/A:1021825418336 ↗
18. Ray · J. Am. Ceram. Soc. · 1996 · 79 · 315510.1111/j.1151-2916.1996.tb08090.x ↗
19. Rebiscoul · J. Nucl. Mater. · 2004 · 326 · 910.1016/j.jnucmat.2003.10.015 ↗