Silver valence and local environments in borosilicate and calcium aluminoborate waste glasses as determined from X-ray absorption spectroscopy

Silver K-edge X-ray absorption near edge structure (XANES) and extended X-ray absorption fine structure (EXAFS) data were collected and analyzed to characterize silver (Ag) environments in borosilicate and Ca-aluminoborate glass formulations developed as potential candidates for the immobilization of certain nuclear wastes. Silver is found in some nuclear waste streams and must be encapsulated in glass during waste vitrification processes. A related concern deals with phase separation within these glasses and whether colloidal silver would be present in the glass melt, which could present processing issues, or in the waste glass product. Characterization of the silver environments provides useful information for optimizing the silver incorporation ability of such glasses. Data were also gathered on four crystalline standards: Ag-foil, Ag{sub 2}O, argentojarosite (AgFe{sub 3}(SO{sub 4}){sub 2}(OH){sub 6}), and AgO. XANES data indicate Ag{sup +} as the dominant species in the glasses. XANES and EXAFS data show that the average Ag environment in the Ca-aluminoborate glass is different compared with those in the two borosilicate glasses investigated. EXAFS analyses show that Ag in the borosilicate glasses is coordinated by two oxygens in a similar environment to that in crystalline Ag{sub 2}O, except that the associated Ag-O distances are approximately 0.10 Angstroms longermore » in the glass. Silver in the Ca-aluminoborate glass may be within one highly disordered site, or possibly, several different sites, where the average Ag-O distance, coordination number, and Debye-Waller factor are larger than those determined for the borosilicate glasses. Despite their relatively high silver contents, there is no evidence from XANES or EXAFS of colloidal silver in the glasses investigated.« less