Influence of heat treatment on spectroscopic properties of Er3+ in multicomponent ZrF4–ZnF2–AlF3–YF3–MF2 (M = Ca, Sr, Ba) based glass

Abstract Er3+ doped multicomponent fluoride based glass was prepared. These precursor fluoride glass samples were then heated using different schedules. Crystalline phase particles were successfully precipitated in the multicomponent fluoride glass samples after heat treatment. The influence of heat treatment on the spectroscopic properties of Er3+ in multicomponent fluoride based glass samples were discussed. Small changes of the Judd–Ofelt parameters Ωi (i = 2, 4, 6) were found in multicomponent fluoride glass samples before and after heat treatment compared to oxyfluoride telluride glass. Preparation conditions used to produce transparent multicomponent fluoride glass ceramics doped with rare-earth ions are discussed.