Mass fractal characteristics of sonogels prepared from sonohydrolysis of tetraethoxysilane with additions of dimethylformamide

Abstract Wet silica gels with ∼1.4 × 10 −3 mol SiO 2 /cm 3 and ∼90 vol.% liquid phase were prepared from the sonohydrolysis of tetraethoxysilane (TEOS) with different additions of dimethylformamide (DMF). Aerogels were obtained by CO 2 supercritical extraction. The samples were studied mainly by small-angle X-ray scattering (SAXS) and nitrogen adsorption. Wet gels exhibit a mass fractal structure with fractal dimension D increasing from 2.23 to 2.35 and characteristic length ξ decreasing from ∼9.4 nm to ∼5.1 nm, as the DMF/TEOS molar ratio is increased from 0 to 4. The supercritical process apparently eliminates some porosity, shortening the fractality domain in the mesopore region and developing an apparent surface/mass fractal (with correlated mass fractal dimension D m ∼ 2.6 and surface fractal dimension D s ∼ 2.3) in the micropore region. The fundamental role of the DMF addition on the structure of the aerogels is to diminish the porosity and the pore mean size, without, however, modify substantially the specific surface area and the average size of the silica particle of the solid network.