Sol–gel synthesis of erbium-doped yttrium silicate glass–ceramics

Abstract Yttrium silicate glasses and glass–ceramics were prepared by the sol–gel process. Yttrium nitrate was added to tetraethyl orthosilicate in amounts representing between 0.2 and 20 mol%, as well as amounts corresponding to the disilicate composition. Some samples were doped with erbium acetate. The solutions underwent gellation in 2–7 days and were dried for 2 weeks. Differential thermal analysis was used to design a multi-step heat treatment to 1000 °C to densify samples to transparent or translucent monoliths. Above 1000 °C, samples crystallized to yttrium disilicate and cristobalite. Phase separation before crystallization influenced the formation of the crystal phases.