Temperature and time-dependent changes of structure in phosphorus containing aluminosilicate liquids and glasses: in situ Raman spectroscopy at high temperature

Abstract The structural role of phosphorus in glasses and liquids of composition Na 2 Si 2 O 5 and Na 1.8 Al 0.2 Si 2 O 5.1 has been studied by in situ Raman spectroscopy in the temperature range 300–1500 K. Spectra collected at room temperature indicate that the majority of phosphorus atoms occur in Na 3 PO 4 and Na 4 P 2 O 7 complexes, as confirmed by bands at ∼935 and ∼1025 cm −1 , respectively. The amplitude of the band at 935 cm −1 decreased relative to that at 1025 cm −1 with the addition of phosphorus. However, for additions of P 2 O 5 > 4 mol%, the relative proportions of these two bands are observed to be dependent on the thermal history of the sample in the molten state. In situ measurements on samples at temperatures above the glass transition demonstrate that temperature-dependent structural changes occur and, furthermore, that there are time-dependent charges at fixed temperature. The principal time-dependent change observed is an increase in the amplitude of the 935 cm −1 band relative to that at 1025 cm −1 with increasing time. At lower temperature the intensity of 935 cm −1 band increases immediately upon cooling, whereas at higher temperature no changes are detected initially, but change occurs after periods of up to 1 h. The kinetics of these time-dependent changes are interpreted to be a consequence of liquid–liquid immiscibility.