Structural characterization and magnetic properties of Al82Fe16TM2 (TM: Ti, Ni, Cu) alloys prepared by mechanical alloying

Abstract In this work, the structural evolution of Al–16 at.%Fe–2 at.%TM (Transition Metals (TM): Ti, Ni, Cu) alloys during mechanical alloying and their magnetic properties were investigated. The evolution of the phase composition and microstructure of the alloys with the milling time was studied using X-ray diffraction (XRD) and Transmission Electron Microscopy (TEM). The phase composition of the alloys was determined using the Rietveld refinement of the XRD profiles. It was shown that the interaction between the components of the powder mixtures during milling started with dissolution of Fe in the Al crystalline lattice and Al in the Fe crystalline lattice. Upon further milling, ferromagnetic AlFe3 (DO3) formed and further transformed into paramagnetic bcc-AlFe and later into an amorphous phase. It was found that the TM alloying elements significantly influence the kinetics of the transformations during milling: the Al82Fe16Ti2 alloy was fully amorphous after 40 h of milling, the Al82Fe16Ni2 alloy required 50 h of milling to achieve complete amorphization, and the Al82Fe16Cu2 alloy was only partially amorphous after 60 h of milling. The interpretation of the observed alloying effect has been proposed. The magnetic properties of the alloys were correlated with the results of the structural characterization.