Preparation and optical properties of Eu3+ doped and Er3+/Yb3+ codoped oxyfluoride glass ceramics containing Ba1− Lu F2+ nanocrystals

Abstract Novel transparent oxyfluoride glass ceramics were prepared and crystal phase evolution from cubic BaF2 to BaxLu1 − xF2 + x was achieved by the gradual substitution LuF3 for BaF2 in the glass compositions in mol% of 65SiO2–14.5B2O3–11.5Na2O–(9–x)BaF2–xLuF3 (x = 0, 1, 2, 3). The corresponding crystallization mechanism was explored according to FTIR and XRD results. The enhanced emission intensity, obvious Stark splitting in the emission spectra and long fluorescence decay lifetimes of Eu3 + ions evidenced the incorporation of Eu3 + ions into the precipitated fluoride nanocrystals. Especially, along with the gradual substitution LuF3 for BaF2, much more Eu3 + ions were partitioned into the precipitated Ba1 − xLuxF2 + x nanocrystals, which provided a novel strategy of controlling the ionic distribution and enhancing the luminescence efficiency of rare earth ions in the oxyfluoride glass ceramics. Temperature dependent characteristics of upconversion luminescence of Er3 +/Yb3 + ions in the oxyfluoride glass ceramics was investigated and a high thermal sensitivity was obtained based on the fluorescence intensity ratio (FIR) technique, which suggested that this material was a promising candidate for the optical temperature sensors.