Diffusion barrier properties of amorphous ZrCN films for copper metallization

Abstract A novel amorphous zirconium carbon nitrides (ZrCN) material was deposited by reactive sputtering using a ZrC target (99.5% in purity) in a mixture of Ar and N 2 ambient. The microstructure and mechanical properties of the ZrCN films were examined with respect to N 2 pressure. For thermal stability characterization, the stacked structure of Cu/ZrCN/Si was subsequently subject to thermal treatments at temperatures from 300 °C to 900 °C for 30 min in a vacuum tube with the base pressure of 3 × 10 −5 torr. The results show that the amorphous ZrCN films exhibit superior mechanical properties to either ZrN or ZrC including hardness and elastic modulus. The stacked samples were shown to be thermally stable up to about 800 °C from Auger electron spectroscopy and X-ray diffraction, where the ZrCN still remains its amorphous phase. The device completely fails at 900 °C and the mechanism is discussed in the paper.