Glass transition temperatures and structures of multicomponent borate glasses: Influence of modifier cation field strengths

Abstract Glass transition temperatures, T g , are determined for a series of multicomponent borate glasses with composition xPbO·(33.33 − x)Na 2 O·yAl 2 O 3 ·1.3ySiO 2 ·(66.67 − 2.3y)B 2 O 3 , (where x and y take values from 0 up to 13.5 mol%, and from 0 up to 5.3 mol%, respectively). For this purpose, differential scanning calorimetry is used while the structure of these glasses containing two kinds of modifier oxides — Na 2 O and PbO, is investigated by infrared spectroscopy. A detailed analysis of the infrared spectra reveals that at constant total content of the glass-forming oxides (B 2 O 3 , SiO 2 and Al 2 O 3 ) in the glasses investigated, the borate network progressively depolymerizes when Na 2 O is substituted for PbO. This substitution favors the destruction of the more rigid structural units and the formation at their expense of units with a lower degree of connectivity. The macroscopic manifestation of these structural changes is the steep decrease in the glass transition temperature of the glasses investigated at increasing PbO concentration. This tendency for depolymerization of the borate network is explained by the influence of the Pb 2 + -cations possessing substantially higher ionic field strength as compared to that of the Na + -cations.