Surface kinetics of nitrogen dissolution and its correlation to the slag structure in the CaO―SiO2, CaO―Al2O3, and CaO―SiO2―Al2O3 slag system

Abstract The kinetics of nitrogen dissolution into molten slag at 1873 K was investigated by an isotope exchange technique. Rate constants were correlated with the molten slag structure obtained from FT-IR spectra. The rate constant in the CaO ― SiO 2 binary system showed a maximum value at a specific slag composition followed by a decrease in the rate due to excess O 2− blocking the surface sites for nitrogen adsorption. The rate constant in the CaO ― Al 2 O 3 binary system was comparatively constant within the experimental range of 45 mass% to 60 mass%. The rate constant in the CaO ― SiO 2 ― Al 2 O 3 ternary slag system was measured within the boundary of the liquidus line and showed a close correlation with the slag structure. Furthermore, the rate constant in the CaO ― SiO 2 ― Al 2 O 3 ternary system was found to be significantly higher compared to the binary system due to the correlated effect of lower binding energies of the Al ― O bonds and the increased number of reaction sites available when smaller Si ― O tetrahedral were simultaneously present with Al ― O bonds.