In situ crystallization of lithium disilicate glass: Effect of pressure on crystal growth rate

Crystallization of a Li2O.2SiO2 (LS2) glass subjected to a uniform hydrostatic pressure of 4.5 GPa and 6 GPa was investigated up to a temperature of 750 C. The density of the compressed glass is about 2% greater at 4.5 GPa than at 1 atm and, depending upon the processing temperature, up to 10% greater at 6 GPa. Crystal growth rates investigated as a function of temperature and pressure show that lithium disilicate crystal growth is an order of magnitude slower at 4.5 GPa than 1 atm resulting in a shift of +45 C (plus or minus 10 C) in the growth rate curve at high pressure compared to 1 atm condition. At 6 GPa lithium disilicate crystallization is suppressed entirely, while a new high pressure lithium metasilicate crystallizes at temperatures 95 C (plus or minus 10 C) higher than those reported for lithium disilicate crystallization at 1 atm. The decrease in crystal growth rate with increasing pressure for lithium disilicate glass up to 750 C is related to an increase in viscosity with pressure associated with fundamental changes in glass structure accommodating densification.