Ag-doped antibacterial porous materials with slow release of silver ions

Abstract The inorganic–organic hybrids of polyethyleneglycol (PEG), tetraethoxysilane (TEOS) and triethylphosphate (TEP) doped by silver ions were prepared by sol–gel method. After molding and heating at 600 °C to remove organic components, porous Ag–P2O5–SiO2 monoliths were obtained. Thermogravimetry (TG), differential thermal analysis (DTA), infrared spectra, ultraviolet–visible (UV–vis) spectra and pore structure of the samples were measured to show that organic components and residual water could be removed by a heat-treatment up to 600 °C and the mesopores with 6 nm pore diameter were formed. Specific surface area and pore volume of the samples were adjusted with different contents of TEP in the starting composition. Ag+ ions could be stably released into water at 30 °C up to 28 days. Antibacterial experiment showed that such materials treated at 600 °C could restrain Escherichia coli effectively.