1.5 μm Emission and infrared-to-visible frequency upconversion in Er+3/Yb+3-doped phosphoniobate glasses

Sodium phosphoniobate glasses with the composition (mol%) 75NaPO 3 -25Nb 2 O 5 and containing 2 mol% Yb 3+ and x mol% Er 3+ (0.01 ≤ x ≤ 2) were prepared using the conventional melting/casting process. Er 3+ emission at 1.5 μm and infrared-to-visible upconversion emission, upon excitation at 976 nm, are evaluated as a function of the Er 3+ concentration. For the lowest Er 3+ content, 1.5 μm emission quantum efficiency was 90%. Increasing the Er 3+ concentration up to 2 mol%, the emission quantum efficiency was observed to decrease to 37% due to concentration quenching. The green and red upconversion emission intensity ratio was studied as a function of Yb 3+ co-doping and the Er 3+ Er 3+ energy transfer processes.