Synthesis and bioactive properties of macroporous nanoscale SiO2–CaO–P2O5 bioactive glass

Abstract A macroporous nanoscale bulk bioactive glass (SiO 2 –CaO–P 2 O 5 system) was prepared by sol–gel co-template method. Porosimeter analysis showed that the as-synthesized bioactive glasses (BGs) had a porosity of 85% and exhibited a multimodal pore size distribution, nanopores (10–40 nm) and macropores (100 nm–10 μm). Morphological and structural characterizations showed the pores were interconnected with pore walls of about 250 nm in width and 1 μm in length. In vitro bioactivity test indicated that the as-synthesized bulk BGs exhibited faster apatite layer formation capability than the conventional sol–gel BGs. Additionally, the deposited layer was identified as hydroxycarbonate apatite, which is similar to the inorganic part of human bone.