Hardness and refractive index of Ca–Si–O–N glasses

Vickers hardness and refractive index was determined for Ca–Si–O–N glasses with 14.6–58 e/o N and 19–42 e/o Ca. By applying slow cooling rates, transparent glasses were obtained for compositions near Ca _9.94Si ₁₀O _17.73N _8.14, while the majority of the glasses were opaque due to small inclusions of elemental Si and/or Ca-silicide. Determined glass densities varied between 2.80 and 3.25 g/cm ³. Hardness was found to vary from 7.3 to 10.1 GPa at a load of 500 g and, respectively increase and decrease linearly with N and Ca content. The refractive index was found to increase linearly with N content from 1.62 to 1.95 and showed no significant dependence on Ca content.