Microstructural and physical properties of the ambient pressure dried hydrophobic silica aerogels with various solvent mixtures

Abstract The experimental results on the microstructural and physical properties of the ambient pressure dried hydrophobic silica aerogels with various solvent mixtures have been reported. The aerogels were prepared with sodium silicate precursor, ammonium hydroxide catalyst, trimethylchlorosilane (TMCS) silylating agent, solvent mixture of methanol–isopropanol (MeOH/IPA) and various aprotic solvent mixtures namely, hexane and benzene (HB), hexane and toluene (HT), hexane and xylene (HX), heptane and benzene (HpB), heptane and toluene (HpT), heptane and xylene (HpX). The physical properties of the aerogels such as % of volume shrinkage, density, % of optical transmission, surface area, % of porosity, pore volume, thermal conductivity and heat capacities of the aerogels were studied. The hydrophobicity of the aerogels was studied by contact angle measurements. The HX and HpX aerogels have been found to be more hydrophobic (contact angle, θ > 155°) than the other aerogels. It has been observed that the % of weight increase is highest (1%) for the HT aerogels and lowest (0.25%) for HpX aerogels by keeping them at 70% humidity for 350 h. Further, the aerogels have been characterized by pore size distribution (PSD), Fourier transform infra red spectroscopy (FTIR) and thermogravimetric and differential thermal (TG-DGA) analysis and transmission electron microscopy (TEM) techniques. The results have been discussed by taking into account the surface tension, vapor pressure, molecular weight and chain length of the solvents. Low density (0.051 g/cc), hydrophobic (165°), transparent (85%), low thermal conductive (0.059 W/m K), low heat capacity (180 kJ/m 3 K) and highly porous (97.38%) silica aerogels were obtained with HpX solvent mixture.