An increased F2-laser damage in ‘wet’ silica glass due to atomic hydrogen: A new hydrogen-related E′-center
Source abstract
Abstract
Abstract A dramatic increase of F2-laser induced room temperature-stable point defects in ‘wet’ synthetic silica glass occurs when irradiation temperature is lowered to 80 K. Contrary to the predictions based on the established models of defect processes, a large part of defects induced at 80 K remains stable also at the room temperature. The intensities of the laser-induced optical absorption bands of the non-bridging oxygen hole centers (2.0 and 4.8 eV) and E′-centers (5.8 eV) are comparable to those created by neutron irradiation (1018 n/cm2). A growth of infrared absorption peak at 2237 cm−1 indicates creation of silicon hydride (SiH) groups. A study of irradiation dose dependences and irradiation efficiency at intermediate temperatures (160 K) suggests a novel radiation damage mechanism by insertion of atomic hydrogen in electronically excited Si–O bond. EPR spectra show E γ ′ -like centers overlapped by a new type of E′-centers, characterized by a hyperfine splitting of 0.08 mT of the low-field peak in the derivative spectrum. The new E′-center is assigned to a silicon dangling bond, with the Si atom bonded by two bridging oxygens and an OH group (‘E′(OH)’). Similar centers have been previously observed on SiO2 surfaces.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Glass properties and applications · Laser Material Processing Techniques · Photorefractive and Nonlinear Optics
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (23)
Show source-provided references
1. Morimoto · Phys. Rev. B · 1999 · 59 · 406610.1103/PhysRevB.59.4066 ↗
2. Hosono · Solid State Commun. · 2002 · 122 · 11710.1016/S0038-1098(02)00118-7 ↗
3. Cannas · Phys. Rev. B · 2004 · 69 · 15320
4. Kajihara · Appl. Phys. Lett. · 2001 · 79 · 175710.1063/1.1404407 ↗
5. Griscom · J. Non-Cryst. Solids · 1984 · 68 · 30110.1016/0022-3093(84)90013-9 ↗
6. Kajihara · Phys. Rev. Lett. · 2002 · 89 · 13550710.1103/PhysRevLett.89.135507 ↗
7. Silin · Fiz. Khim. Stekla · 1978 · 4 · 405
8. In most experiments, type ES silica from Tosoh Quartz Inc. was used. To check consistency, separate samples from other manufacturers (Corning, Heraeus) were also studied, giving similar results.
9. Griscom · Phys. Rev. B · 1979 · 20 · 182310.1103/PhysRevB.20.1823 ↗
10. Weil · 1996
11. Data not shown. More detailed experimental data will be reported elsewhere.
12. Griscom · J. Ceram. Soc. Jpn. · 1991 · 99 · 92310.2109/jcersj.99.923 ↗
13. Skuja · Proc. XX Int. Congr. Glass Kyoto · 2004
14. Skuja · J. Non-Cryst. Solids · 1984 · 63 · 43110.1016/0022-3093(84)90111-X ↗
15. Morimoto · J. Non-Cryst. Solids · 1992 · 139 · 3510.1016/S0022-3093(05)80803-8 ↗
16. Zheng · J. Non-Cryst. Solids · 1999 · 258 · 7810.1016/S0022-3093(99)00516-5 ↗
17. Skuja · Proc. SPIE · 2001 · 4347 · 15510.1117/12.425020 ↗
18. Two simulation programs, Bruker SimFonia (manual parameter adjustment) and self- developed software (computer optimized parameters) were used. While the results were similar, a slightly better fit was achieved by the self-developed program, its output is used in this paper.
19. Tsai · J. Non-Cryst. Solids · 1987 · 91 · 7010.1016/S0022-3093(87)80300-9 ↗
20. Agnello · J. Appl. Phys. · 2001 · 89 · 600210.1063/1.1369398 ↗
21. Radtsig · Chem. Phys. Reports · 2000 · 19 · 17
22. Pacchioni · Phys. Rev. B · 1998 · 58 · 774510.1103/PhysRevB.58.7745 ↗
23. Bobyshev · Kinetics Catal. · 1988 · 29 · 551