Preparation of alumina–hercynite nano-spinel via one-step thermal conversion of Fe-doped metal–organic framework MIL-53(Al)

Alumina–hercynite nano-spinel powders were prepared via one-step pyrolysis of iron-acetylacetone-doped Al-based metal–organic framework (MOF), i.e., MIL-53(Al). Organic ferric source, iron acetylacetone, was incorporated in situ into the framework of MIL-53(Al) during the solvothermal synthesis process. Under high-temperature pyrolysis, alumina derived from the MIL-53(Al) matrix and ferric oxides originated from the decomposition of organic ferric precursor in the framework were thermally converted into hercynite (FeAl2O4). The prepared samples were characterized using transmission electron microscopy, X-ray diffraction, N2 sorption, thermogravimetry, Raman spectroscopy and X-ray photoelectron spectroscopy. The final products were identified to be composed of alumina, hercynite and trace amounts of carbon depending on pyrolysis temperature. The experimental results showed that hercynite phase can be obtained and stabilized at low temperatures between 900 and 1100 °C under inert atmosphere. The final products were composed of nano-sized particles with an average size below 100 nm of individual crystal and specific surface areas of 18–49 m2 g−1. © 2016, Springer Science+Business Media Dordrecht.