Silver nanocombs and branched nanowires formation in aqueous binary surfactants solution

Branched nanocrystals, particularly nanocombs, are a unique 1D-morphology that is normally formed in polytypic materials, such as ZnO, and rarely occurs in the highly symmetric fcc metallic system. Here, we report the chemical synthesis of nanocombs of a highly symmetrical fcc silver system that is realized by reducing the silver ions in the presence of a mixture of silver nanoseeds and binary surfactants, namely cetyltrimethylammonium bromide (CTAB) and hexamethylenetetramine (hexamine or HMT), under an alkaline condition. The silver nanocombs feature a high-degree branching orientation toward a single direction with good branch-to-branch spacing. The nanocombs formation was very sensitive to the concentrations of CTAB, HMT and NaOH in the reaction in which, in a typical case, nanocombs or curly nanowires were produced by controlling the concentration of these chemicals in the reaction. We hypothesized that the branching could be due to: (i) a kind of polytypism in such highly symmetrical fcc nanocrystals that was enabled by a selective surfactant adhesion process on the growing crystalline plane and (ii) lattice defects or twinning induced growth redirection in the nanocrystals. The silver nanocombs might generate a peculiar characteristic that is probably superior to those produced by other morphologies, such as nanorods, nanowires, and so on. Thus, it should find extensive use in the currently existing applications.