Nanostructures of sodium titanate/zirconium oxide

In this work is reported the synthesis of nanotubes and nanoribbons from mixed oxides (Ti1−x Zr x O2·nH2O), employing hydrothermal treatment in a highly alkaline medium. The morphology and crystal structure of the products obtained via hydrothermal treatment depend on the value of x. For example, for x equal to 0 and 0.50 were observed the presence of nanotubes (diameter around 9 nm) and nanoribbons (diameter around 200 nm), respectively. However, for x values above 0.50, there was no morphological change. Regarding the crystalline structure of these samples, for x equal to 0 was observed the sodium titanate phase; already for x values up to 0.50, we observed the presence of two crystalline phases: sodium titanate and tetragonal ZrO2. For x values above 0.50, only tetragonal ZrO2 was observed. Furthermore, only the product obtained from x equal to 0.15 was observed the presence of three-dimensional flower-like arrangements. The results obtained by the characterization techniques showed the segregation of zirconium after hydrothermal treatment of precursors with x less or equal to 0.50. Thus, we describe the important role that Ti/Zr molar ratio of the precursor plays on the morphology and crystalline phase of the products formed by hydrothermal treatment.