Preparation and characterization of complex ferrite nanoparticles by a polymer-pyrolysis route
Source abstract
Abstract
The polymer-pyrolysis route used in this work was to synthesize the copolymeric precursor of the mixed metallic ions and then to pyrolyze the precursor into complex spinel ferrite nanoparticles. Thermogravimetric analysis (TGA) showed that the complex ferrite nanoparticles could be obtained by calcination of their precursors at 500°C. The structures, elemental analyses and particle morphology of the as-calcined products were characterized by powder X-ray diffraction (XRD), ICP-AES, transmission electron microscope (TEM) and electron diffraction (ED) pattern. The results revealed that the as-calcined powders were complex spinel ferrites and the size of those nanoparticles ranged from 10 to 20 nm. Magnetic measurements were carried out at room temperature using a vibrating sample magnetometer (VSM). The saturation magnetization of the Mn–Zn ferrites was related to the molar ratio of Mn to Zn and increased with the increase of Mn. The complex Co–Mn–Zn ferrite nanoparticles showed a high magnetization of 58 emu/g at the applied field of 10 kOe and a low coercivity of 30 Oe, which indicated that this materials exhibited characteristics of soft ferromagnetism.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Magnetic Properties and Synthesis of Ferrites · Iron oxide chemistry and applications · Electromagnetic wave absorption materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (24)
Show source-provided references
1. Arulmurugan R., B. Jeyadevan, G. Vaidyanathan, 2005. Effect of Zinc Substitution on Co–Zn and Mn–Zn Ferrite Nanoparticles Prepared by Co-pecipitation. J. Magn. Magn. Mater. 288, 470–47710.1016/j.jmmm.2004.09.138 ↗
2. Cannas C., A. Musinu, D. Peddis, G. Piccaluga, 2004. New Synthesis of Ferrite-silica Nanocomposites by a Sol-gel Auto-combustion. J. Nanopart. Res. 6, 223–23210.1023/B:NANO.0000034679.22546.d7 ↗
3. Drofenik M., A. Znidarsic, M. Kristl A. Kosak, D. Makovec, 2003. Dispersant-assisted Hydrothermal Synthesis of Mn–Zn Ferrites from Raw Oxides. J. Mater. Sci. 38, 3063–306710.1023/A:1024704625296 ↗
4. Kikukawa N., M. Takemori, Y. Nagano, M. Sugasawa, S. Kobayashi, 2004. Synthesis and Magnetic Properties of Nanostructured Spinel Ferrites Using a Glycine-nitrate Process. J. Magn. Magn. Mater. 284, 206–21410.1016/j.jmmm.2004.06.039 ↗
5. Kodama R.H., 1999. Magnetic Nanoparticles. J. Magn. Magn. Mater. 200, 359–37210.1016/S0304-8853(99)00347-9 ↗
6. Mandal K., S.P. Mandal, P. Agudo, M. Pal, 2001. A Study of Nanocrystalline Mn–Zn Ferrite in SiO2 Matrix. Appl. Surf. Sci. 182, 386–38910.1016/S0169-4332(01)00455-X ↗
7. Mangalaraja R.V., S. Ananthakmar, P. Manohar, F.D. Gnanam, M. Awano, 2004. Characterization of Mn0.8Zn0.2Fe2O4 Synthesized by Flash Combustion Technique. Mater. Sci. Eng. A 367, 301–30510.1016/j.msea.2003.10.283 ↗
8. Moulin J., Y. Champion, J.M. Greneche, F. Mazaleyrat, 2003. Magnetic Properties of MnZn Ferrite with Ultra-fine Grain Structure. J. Magn. Magn. Mater. 254, 538–54010.1016/S0304-8853(02)00858-2 ↗
9. Moulin J., Y. Champion, L.K. Varga, J.M. Greneche, F. Mazaleyrat, 2002. Magnetic Properties of Nanocomposites Containing Fe–Ni or Fe Dispersed in a Mn–Zn Ferrite Matrix. IEEE Trans. Magn. 38, 3015–301710.1109/TMAG.2002.802120 ↗
10. Lin W.H., C.S. Hwang, 2002. Characteristics of Powder and Sintered Bodies of Hydrothermally Synthesized Mn–Zn Ferrites. J. Mater. Sci. 37, 1067–107510.1023/A:1014376620601 ↗
11. Lin W.H., S.K.J. Jean, C.S. Hwang, 1999. Phase Formation and Composition of Mn–Zn Ferrite Powders Prepared by Hydrothermal Method. J. Mater. Res. 14, 204–20810.1557/JMR.1999.0030 ↗
12. Lin W.H., S.K.J. Jean, C.S. Hwang, 2000. Powder Characterization and Sinterability of Hydrothermally Synthesized Mn–Zn Ferrites. J. Ceram. Soc. Japan 108, 10–1610.2109/jcersj.108.10 ↗
13. Liu X.M., S.Y. Fu, H.M. Xiao, C.J. Huang, 2005. Synthesis of Nanocrystalline Spinel CoFe2O4 Via a Polymer-pyrolysis Route. Physica B 370, 14–2110.1016/j.physb.2005.08.030 ↗
14. Poddar P., H. Srikanth, S.A. Morrison, E.E. Carpenter, 2005. Inter-particle Interactions and Magnetism in Manganese–Zinc Ferrite Nanoparticles. J. Magn. Magn. Mater. 288, 443–45110.1016/j.jmmm.2004.09.135 ↗
15. Raj K., R. Moskowitz, 1990. Commercial Applications of Ferrofluids. J. Magn. Magn. Mater. 85, 233–24510.1016/0304-8853(90)90058-X ↗
16. Rath C., S. Anand, R.P. Das, K.K. Sahu, S.D. Kulkarni, S.K. Date, N.C. Mishra, 2002. Dependence on Cation Distribution of Particle Size, Lattice Parameter, and Magnetic Properties in Nanosize Mn–Zn Ferrite. J. Appl. Phys. 91, 2211–221510.1063/1.1432474 ↗
17. Son S., R. Swaminathan, M.E. McHenry, 2003. Structure and Magnetic Properties of rf Thermally Plasma Synthesized Mn and Mn–Zn Ferrite Nanoparticles. J. Appl. Phys. 93, 7495–749710.1063/1.1557953 ↗
18. Thakur A., M. Singh, 2003. Preparation and Characterization of Nanosize Mn0.4Zn0.6Fe2O4 Ferrite by Citrate Precursor Method. Ceram. ntern. 29:505–51110.1016/S0272-8842(02)00194-3 ↗
19. Verma A., T.C. Goel, R.G. Mendiratta, M.I. Alam, 1999. Dielectric Properties of NiZn Ferrites Prepared by the Citrate Precursor Method. Mater. Sci. Eng. B 60, 156–16210.1016/S0921-5107(99)00019-7 ↗
20. Wang J., C. Zeng, Z. Peng, Q. Chen, 2004. Synthesis and Magnetic Properties of Zn1−xMnxFe2O4 Nanoparticles. Physica B 349, 124–12810.1016/j.physb.2004.02.014 ↗
21. Yener D.O., H. Giesche, 2001. Synthesis of Pure and Manganese-, Nickel-, and Zinc-doped Ferrite Particles in Water-in-oil Microemulsions. J. Am. Ceram. Soc, 84, 1987–199510.1111/j.1151-2916.2001.tb00947.x ↗
22. Yu L.H., H.X. Yang, X.P. Ai, Y.L. Cao, 2005. Structural and Electrochemical Characterization of Nanocrystalline Li[Li0.12Ni0.32Mn0.56]O2 Synthesized by a Polymer-Pyrolysis Route. J. Phys. Chem. B 109, 1148–115410.1021/jp0464369 ↗
23. Yu L.H., Y.L. Cao, H.X. Yang, X.P. Ai, Y.Y. Ren, 2004. Preparation and Electrochemical Characterization of Nanocrystalline Li[Li0.12Ni0.32Mn0.56]O2 Pyrolyzed from Polyacrylate Salts. Mater. Chem. Phys. 88, 353–35610.1016/j.matchemphys.2004.07.023 ↗
24. Zhao X.Y., B.C. Zheng, H.C. Gu, 1999. Preparation of Phase Homogeneous Mn–Zn Ferrite Powder by Spray Pyrolysis. J. Mater. Res. 14, 3073–308210.1557/JMR.1999.0412 ↗