Nanosphere dispersion on a large glass substrate by low dose ion implantation for localized surface plasmon resonance

Dispersing nanospheres on a large glass substrate is the key to fabricate noble metal nanostructures for localized surface plasmon resonance through dispersed nanosphere lithography. This article reports that by modifying the glass surface with low dose ion implantation and successively dip coating the surface with poly(diallyldimethyl ammonium chloride) (PDDA), polystyrene or silica nanospheres can be dispersed on a large glass substrate. Investigation shows that several kinds of ions, such as silicon, boron, argon, and arsenic, can improve the nanosphere dispersion on glass, attributed to the ion bombardment-caused silicon increment. Ion implantation imposes no surface roughness or optical loss to the glass substrate, thus this method is suitable for localized surface plasmon resonance application. Experiments show silicon ion implantation can best disperse the nanospheres. For the gold nanostructures obtained by obliquely evaporating 30 nm of gold film onto the polystyrene nanospheres, which are dispersed on a silicon ion implanted glass substrate, a localized surface plasmon resonance sensitivity of 242 nm/RIU is achieved.