Designing copper–zirconium based nanowires for improving yield strength and plasticity by configuring surface atoms
Source abstract
Abstract
Epitaxial-Bain-Path and Uniaxial-Bain-Path studies reveal that a B2-CuZr nanowire with Zr atoms on the surface is energetically more stable compared to a B2-CuZr nanowire with Cu atoms on the surface. Nanowires of cross-sectional dimensions in the range of ~20–50 A are considered. Such stability is also correlated with the initial state of stress in the nanowires. It is also demonstrated here that a more stable structure, i.e., B2-CuZr nanowire with Zr atoms at surface shows improved yield strength compared to B2-CuZr nanowire with Cu atoms at surface site, over range of temperature under both the tensile and the compressive loadings. Nearly 18% increase in the average yield strength under tensile loading and nearly 26% increase in the averaged yield strength under compressive loading are observed for nanowires with various cross-sectional dimensions and temperatures. It is also observed that the B2-CuZr nanowire with Cu atom at the surface site shows a decrease in failure/plastic strain with an increase in temperature. On the other hand, B2-CuZr nanowires with Zr at the surface site shows an improvement in failure/plastic strain, specially at higher temperature as compared to the B2-CuZr nanowires which are having Cu atoms at the surface site. Finally, a possible design methodology for an energetically stable nano-structure with improved thermo-mechanical properties via manipulating the surface atom configuration is proposed.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Aluminum Alloys Composites Properties · Electrodeposition and Electroless Coatings · Nanoporous metals and alloys
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. Alippi P, Marcus PM, Scheffler M (1997) Strained tetragonal states and Bain paths in metals. Phys Rev Lett 78:389210.1103/PhysRevLett.78.3892 ↗
2. Cheng YQ, Ma E, Sheng HW (2008) Alloying strongly influences the structure, dynamics, and glass forming ability of metallic supercooled liquids. Appl Phys Lett 93:11191310.1063/1.2987727 ↗
3. Clausius R (1870) On a mechanical theorem applicable to heat. Phil Mag 40:122–12710.1080/14786447008640370 ↗
4. Das J, Tang MB, Kim KB, Theissmann R, Baier F, Wang WH et al (2005) “Work-hardenable” ductile bulk metallic glass. Phys Rev Lett 94:20550110.1103/PhysRevLett.94.205501 ↗
5. Diao J, Gall K, Dunn ML (2003) Surface-stress-induced phase transformation in metal nanowires. Nat Mater 2(10):656–66010.1038/nmat977 ↗
6. Duan G, Lind ML, Blauwe KD, Wiest A, Johnson WL (2007) Thermal and elastic properties of Cu–Zr–Be bulk metallic glass forming alloys. Appl Phys Lett 90:211900110.1063/1.2741050 ↗
7. Fang J, You H, Kong P, Ding B, Song X (2008) Size-dependent structure transformation from amorphous phase to crystal. Appl Phys Lett 92:14311110.1063/1.2907325 ↗
8. Finnis MW, Sinclair JE (1984) A simple N-body potential for transition metals. Philos Mag A 50:4510.1080/01418618408244210 ↗
9. Hoover WG (1985) Canonical dynamics: equilibrium phase-space distributions. Phys Rev A 31:1695–169710.1103/PhysRevA.31.1695 ↗
10. Inoue A (2002) Stabilization of metallic supercooled liquid and bulk amorphous alloys. Acta Mater 48:27910.1016/S1359-6454(99)00300-6 ↗
11. Inoue A, Takeuchi A (2002) Recent progress in bulk glassy alloys: bulk amorphous, nano-crystalline and nano-quasicrystalline alloys IV. Mater Trans, JIM 43:189210.2320/matertrans.43.1892 ↗
12. Inoue A, Zhang W (2004) Formation, thermal stability and mechanical properties of Cu–Zr and Cu–Hf binary glassy alloy rods. Mater Trans 45:58410.2320/matertrans.45.584 ↗
13. Inoue A, Zhang T, Masumoto T (1990) Production of amorphous cylinder and sheet of La55Al25Ni20 alloy by a metallic mold casting method. Mater Trans, JIM 31:42510.2320/matertrans1989.31.425 ↗
14. Inoue A, Zhang W, Zhang T, Kurosaka K (2001) High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems. Acta Mater 49:264510.1016/S1359-6454(01)00181-1 ↗
15. Jakse N, Pasturel A (2008) Glass forming ability and short-range order in a binary bulk metallic glass by ab initio molecular dynamics. Appl Phys Lett 93:11310410.1063/1.2976428 ↗
16. Johnson WL (1999) Bulk glass-forming metallic alloys: science and technology. Mater Res Bull 24:4210.1557/S0883769400053252 ↗
17. Kim KB, Das J, Baier F, Tang MB, Wang HW, Eckert J (2006) Heterogeneity of a Cu47.5Zr47.5Al5 bulk metallic glass. Appl Phys Lett 88:05191110.1063/1.2171472 ↗
18. Kumar G, Ohkubo T, Mukai T, Hono K (2007) Plasticity and microstructure of Zr–Cu–Al bulk metallic glasses. Scripta Mater 57:17310.1016/j.scriptamat.2007.02.013 ↗
19. LAMMPS (2010) http://www.cs.sandia.gov/~sjplimp/lammps.html
20. Lekka CE, Ibenskas A, Yavari AR, Evangelakis GA (2007) Tensile deformation accommodation in microscopic metallic glasses via subnanocluster reconstructions. Appl Phys Lett 91:21410310.1063/1.2816912 ↗
21. Lund AC, Schuh CA (2003) Atomistic simulation of strain-induced amorphization. Appl Phys Lett 82:1310.1063/1.1534942 ↗
22. Mclellan AG (1974) Virial theorem generalized. Am J Phys 42:239–24310.1119/1.1987655 ↗
23. Mendelev MI, Ackland GJ (2007) Development of an interatomic potential for the simulation of phase transformations in zirconium. Phil Mag Letts 87(5):349–35910.1080/09500830701191393 ↗
24. Nose SA (1984) A unified formulation of the constant temperature molecular dynamics methods. J Chem Phys 81:511–51910.1063/1.447334 ↗
25. Pauly S, Das J, Mattern N, Kim D H, Eckert J (2009) Phase formation and thermal stability in Cu–Zr–Ti(Al) metallic glasses Intermetallics 17(6):453–46210.1016/j.intermet.2008.12.003 ↗
26. Peker A, Johnson WL (1993) A highly processable metallic glass: Zr41. 2Ti13. 8Cu12. 5Ni10. 0Be22. 5. Appl Phys Lett 63:234210.1063/1.110520 ↗
27. Plimpton SJ (1995) Fast parallel algorithms for short-range molecular dynamics. J Comput Phys 117:1–1910.1006/jcph.1995.1039 ↗
28. Sutrakar VK, Mahapatra DR (2008) Formation of stable ultra-thin pentagon Cu nanowires under high strain rate loading. J Phys: Condens Matter 20:33520610.1088/0953-8984/20/33/335206 ↗
29. Sutrakar VK, Mahapatra DR (2009a) Coupled effect of size, strain rate, and temperature on the shape memory of a pentagonal Cu nanowire. Nanotechnology 20:04570110.1088/0957-4484/20/4/045701 ↗
30. Sutrakar VK, Mahapatra DR (2009b) Stress-induced phase transformation and pseudo-elastic/pseudo-plastic recovery in intermetallic Ni–Al nanowires. Nanotechnology 20:29570510.1088/0957-4484/20/29/295705 ↗
31. Sutrakar VK, Mahapatra DR (2009c) Stress-induced martensitic phase transformation in Cu–Zr nanowires. Mater Lett 63:1289–129210.1016/j.matlet.2009.02.064 ↗
32. Sutrakar VK, Mahapatra DR (2009d) Comment on “Pseudoelasticity of Cu–Zr nanowires via stress-induced martensitic phase transformations”. Appl Phys Lett 95:13610110.1063/1.3242021 ↗
33. Sutrakar VK, Mahapatra DR (2010) Single and multi-step phase transformation in CuZr nanowire under compressive/tensile loading. Intermetallics 18:679–68710.1016/j.intermet.2009.11.006 ↗
34. Sutrakar VK, Mahapatra DR (2011) Universal stability and temperature dependent phase transformation in group VIIIB-IB transition metal FCC nanowires. J Phys Chem C 115:10394–1039810.1021/jp2006815 ↗
35. Swenson RJ (1983) Comments on virial theorems for bounded systems. Am J Phys 51:940–94210.1119/1.13390 ↗
36. Tsai DH (1979) The virial theorem and stress calculation in molecular dynamics. J Chem Phys 70:1375–138210.1063/1.437577 ↗
37. Wang WH, Dong C, Shek HC (2004) Bulk metallic glasses. Mater Sci Eng, R 44:4510.1016/j.mser.2004.03.001 ↗
38. Wang XD, Yin S, Cao QP, Jiang JZ, Franz H, Jin JH (2008) Atomic structure of binary Cu64.5Zr35.5 bulk metallic glass. Appl Phys Lett 92:01190210.1063/1.2828694 ↗
39. Zhang T, Inoue A, Masumoto T (1991) Amorphous Zr–Al–TM (TM = Co, Ni, Cu) alloys with significant supercooled liquid region of over 100 K. Mater Trans, JIM 32:100510.2320/matertrans1989.32.1005 ↗
40. Zhou M (2003) A new look at the atomic level virial stress: on continuum-molecular system equivalence. Proc R Soc A 459:2347–239210.1098/rspa.2003.1127 ↗