The Effect of Hydrolysis Temperature on Synthesis of Bimodally Nanostructured Porous Titania

Bimodally porous (2–4 and 20–100 nm) titania powders were prepared by hydrolysis of titanium tetraisopropoxide (TTIP), and the effect of hydrolysis temperature on the phase transformation and pore structure was investigated. The phase transformation was slightly retarded with increasing hydrolysis temperature, when the initial water concentration was small. The evolution of particle phase composition from amorphous to crystalline anatase and rutile was largely proportional to the calcination temperature and the initial water concentration. The pore size distribution was bimodal with fine intra-particle pores (2–4 nm in diameter) and larger inter-particle pores (20–100 nm). The intra-particle pores decreased in diameter at the hydrolysis temperature of 20°C. The specific surface area (SSA) of the dried powders ranged from 253 to 587 m2/g and the highest SSA was obtained at the hydrolysis temperature of 20°C.