Effect of the La(OH)3 preparation method on the surface and rehydroxylation properties of resulting La2O3 nanoparticles
Source abstract
Abstract
Several lanthanum hydroxides (28–146 m2/g) were prepared by different procedures involving precipitation and hydrothermal methods by conventional heating or with microwaves. The use of ultrasounds during precipitation led to the formation of additional crystalline phases whereas the aging treatment with microwaves decreased the temperature needed to form the lanthanum oxide phase when compared with the samples aged by conventional heating. After calcination, La2O3 samples showed similar BET surface areas (3–5 m2/g) but different particle sizes ranging from 150 to 600 nm depending on the La(OH)3 preparation method, as observed by TEM. La2O3 samples were completely rehydroxylated after 80 h of exposure to atmospheric air at controlled humidity conditions recovering only partially the surface areas of the La(OH)3 precursors (14–18 m2/g). The progress of rehydroxylation with time occurred in several steps at different rates. Rehydroxylation rate mainly depended on the particle size and surface area of the lanthanum oxide sample. Therefore, the method used to prepare the initial lanthanum hydroxide affects the surface and rehydroxylation properties of the subsequent lanthanum oxide sample.
Source: openaire · Quality: candidate unverified · Source record ↗
Research context
OpenAlex topics: Catalytic Processes in Materials Science · Catalysis and Oxidation Reactions · Luminescence Properties of Advanced Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (34)
Show source-provided references
1. Bergadà O, Vicente I, Salagre P, Cesteros Y, Medina F, Sueiras JE (2007) Microporous Mesoporous Mater 101:363–37310.1016/j.micromeso.2006.11.033 ↗
2. Bernal S, Díaz JA, García R, Rodríguez-Izquierdo JM (1985) Study of some aspects of the reactivity of lanthanum oxide with carbon dioxide and water. J Mater Sci 20:537–54110.1007/BF01026524 ↗
3. Bernal S, Botana FJ, García R, Rodríguez-Izquierdo JM (1987) Behavior of rare earth sesquioxides exposed to atmospheric carbon dioxide and water. React Solids 4:23–4010.1016/0168-7336(87)80085-2 ↗
4. Cesteros Y, Salagre P, Medina F, Sueiras JE (1999) Several factors affecting faster rates of gibbsite formation. Chem Mater 11:123–12910.1021/cm980527z ↗
5. Dakhel AA (2007) Structural and ac electrical properties of oxidised La and La–Mn thin films grown on Si substrates. Mater Chem Phys 102:266–27010.1016/j.matchemphys.2007.01.002 ↗
6. Djerdj I, Garnweitner G, Su DS, Niederberger M (2007) Morphology-controlled nonaqueous synthesis of anisotropic lanthanum hydroxide nanoparticles. J Solid State Chem 180:2154–216510.1016/j.jssc.2007.05.019 ↗
7. Fleisch TH, Hicks RF, Bell AT (1984) An XPS study of metal-support interactions on PdSiO2 and PdLa2O3. J Catal 87:398–41310.1016/0021-9517(84)90200-8 ↗
8. Fleming P, Farrell RA, Holmes JD, Morris MA (2010) The rapid formation of La(OH)3 from La2O3 powders on exposure to water vapour. J Am Ceram Soc 93:1187–119410.1111/j.1551-2916.2009.03564.x ↗
9. Gobichon AE, Auffrédic JP, Louër D (1996) Thermal decomposition of neutral and basic lanthanum nitrates studied with temperature-dependent powder diffraction and thermogravimetric analysis. Solid State Ion 93:51–6410.1016/S0167-2738(96)00498-5 ↗
10. Hu C, Liu H, Dong W, Zhang Y, Bao G, Lao C, Whang ZL (2007) La(OH)3 and La2O3 nanobelts—synthesis and physical properties. Adv Mater 19:470–47410.1002/adma.200601300 ↗
11. Jiawen D, Yanli W, Weili S, Youngxiu L (2006) Preparation of La(OH)3 and La2O3 with Rod Morphology by Simple Hydration of La2O3. J Rare Earths 24:440–44210.1016/S1002-0721(06)60139-7 ↗
12. Kale SS, Jadhav KR, Patil PS, Gujar TP, Lokhande CD (2005) Characterizations of spray-deposited lanthanum oxide (La2O3) thin films. Mater Lett 59:3007–300910.1016/j.matlet.2005.02.091 ↗
13. Kim SJ, Han WK, Kang SG, Han MS, Cheong YH (2008) Formation of lanthanum hydroxide and oxide via precipitation. Solid State Phenom 135:23–2610.4028/www.scientific.net/SSP.135.23 ↗
14. Klingenberg B, Vannice MA (1996) Influence of pretreatment on lanthanum nitrate, carbonate, and oxide powders. Chem Mater 8:2755–276810.1021/cm9602555 ↗
15. Ma X, Zhang H, Ji Y, Xu J, Yang D (2004) Synthesis of ultrafine lanthanum hydroxide nanorods by a simple hydrothermal process. Mater Lett 58:1180–118210.1016/j.matlet.2003.08.031 ↗
16. Méndez M, Carvajal JJ, Cesteros Y, Aguiló M, Díaz F, Giguère A, Drouin D, Martínez-Ferrero E, Salagre P, Formentín P, Pallarès J, Marsal LF (2010) Sol–gel Pechini synthesis and optical spectroscopy of nanocrystalline La2O3 doped with Eu3+. Opt Mater 32:1686–169210.1016/j.optmat.2010.02.018 ↗
17. Méndez M, Cesteros Y, Marsal LF, Martínez-Ferrero E, Salagre P, Formentín P, Pallarès J, Aguiló M, Díaz F, Carvajal JJ (2011) Polymer composite P3HT:Eu3+ doped La2O3 nanoparticles as a down-converter material to improve the solar spectrum energy. Opt Mater 33:1120–112310.1016/j.optmat.2010.09.001 ↗
18. Méndez M, Cesteros Y, Marsal LF, Giguère A, Drouin D, Salagre P, Formentín P, Pallarès J, Aguiló M, Díaz F, Carvajal JJ (2012) Effect of thermal annealing on the kinetics of rehydroxylation of Eu3+:La2O3 nanocrystals. Inorg Chem 51:6139–614610.1021/ic300108f ↗
19. Mentus S, Jelic D, Grudic V (2007) Lanthanum nitrate decomposition by both temperature programmed heating and citrate gel combustion comparative study. J Therm Anal Calorim 90:393–39710.1007/s10973-006-7603-5 ↗
20. Murugan AV, Navale SC, Ravi V (2006) Synthesis of nanocrystalline La2O3 powder at 100°C. Mater Lett 60:848–84910.1016/j.matlet.2005.10.030 ↗
21. Neumann A, Walter D (2006) The thermal transformation from lanthanum hydroxide to lanthanum hydroxide oxide. Therm Acta 445:200–20410.1016/j.tca.2005.06.013 ↗
22. Ozawa M, Onoe R, Kato H (2006) Formation and decomposition of some rare earth (RE = La, Ce, Pr) hydroxides and oxides by homogeneous precipitation. J Alloy Compd 408–412:556–55910.1016/j.jallcom.2004.12.073 ↗
23. Rosynek MP, Magnuson DT (1977) Preparation and characterization of catalytic lanthanum oxide. J Catal 46:402–41310.1016/0021-9517(77)90224-X ↗
24. Rzączyńska Z, Ostasz A, Pikus S (2005) Thermal properties of rare earth elements complexes with 1,3,5-benzenetricarboxylic acid. J Therm Anal Calorim 82:347–35110.1007/s10973-005-0901-5 ↗
25. Sax NI, Lewis JR (eds) (1987) Hawley’s condensed chemical dictionary, 11th edn. Van Nostrand Reinhold, New York, p 683
26. Van TL, Che M, Tatibouet JM, Kermarec M (1993) Infrared study of the formation and stability of La2O2CO3 during the oxidative coupling of methane on La2O3. J Catal 142:18–2610.1006/jcat.1993.1185 ↗
27. Wang X, Li Y (2003) Rare-earth-compound nanowires, nanotubes, and fullerene-like nanoparticles: synthesis, characterization, and properties. Chem Eur J 9:5627–563510.1002/chem.200304785 ↗
28. Wang X, Wang M, Song H, Ding B (2006) A simple sol–gel technique for preparing lanthanum oxide nanopowders. Mater Lett 60:2261–226510.1016/j.matlet.2005.12.142 ↗
29. Wang S, Zhao Y, Chen J, Xu R, Luo L, Zhong S (2010) Self-assembled 3D La(OH)3 and La2O3 nanostructures: fast microwave synthesis and characterization. Superlattices Microstruct 47:597–60510.1016/j.spmi.2010.02.002 ↗
30. Wang L, Ma Y, Wang Y, Liu S, Deng Y (2011) Efficient synthesis of glycerol carbonate from glycerol and urea with lanthanum oxide as a solid base catalyst. Catal Commun 12:1458–146210.1016/j.catcom.2011.05.027 ↗
31. Yamamoto O, Takeda Y, Kanno R, Fushimi M (1985) Thermal decomposition and electrical conductivity of M(OH)3 and MOOH (M = Y, lanthanide). Solid State Ion 17:107–11410.1016/0167-2738(85)90057-8 ↗
32. Zhang N, Yi R, Zhou L, Gao G, Shi R, Qiu G, Liu X (2009) Lanthanide hydroxide nanorods and their thermal decomposition to lanthanide oxide nanorods. Mater Chem Phys 114:160–16710.1016/j.matchemphys.2008.09.004 ↗
33. Zhu JL, Zhou YH, Yang HX (1997) Effects of lanthanum and neodymium hydroxides on secondary alkaline zinc electrode. J Power Sour 69:169–17310.1016/S0378-7753(97)02569-X ↗
34. Zhu J, Gui Z, Ding Y (2008) A simple route to lanthanum hydroxide nanorods. Mater Lett 62:2373–237610.1016/j.matlet.2007.12.002 ↗