Magnetic properties of iron oxide nanoparticles prepared by seeded-growth route

In this work we investigate the magnetic properties of iron oxide nanoparticles obtained by two-step synthesis (seeded-growth route) with sizes that range from 6 to 18 nm. The initial seeds result monocrystalline and exhibit ferromagnetic behavior with low saturation field. The subsequent growth of a shell enhances the anisotropy inducing magnetic frustration, and, consequently, reducing its magnetization. This increase in anisotropy occurs suddenly at a certain size (similar to 10 nm). Electronic and structural analysis with X-ray absorption spectroscopy indicates a step reduction in the oxidation state as the particle reaches 10 nm size while keeping its overall structure in spite of the magnetic polydispersity. The formation of antiphase magnetic boundaries due to island percolation in the growing shells is hypothesized to be the mechanism responsible of the magnetic behavior, as a direct consequence of the two-step synthesis route of the nanoparticles.