3D crosslinked and interlocked graphene nanointerface enables ultra-tough and strong alumina

The mechanics of structural ceramics, especially the toughness, are crucial to their service reliability and need to be continuously optimized. Inspired by the “brick-mortar” structure and further adjusting the microstructure of “mortar” on the interface, ceramic with strength and toughness up to 444.16 MPa and 13.79 MPa⋅m 1/2 is constructed by hot pressed sintering with alumina (Al 2 O 3 ) as brick and vertical graphene (VG) with active atomic edges as mortar. Relying on the covalent interface between VG grown in-situ and Al 2 O 3 , the sliding of Al 2 O 3 links the shear-deformation process of the crosslinked and interlocked nanointerface formed by VG, making the VG-enhanced Al 2 O 3 ceramics (AVG) obtain super toughness. Moreover, the structure of interlocked VG-nanointerface exhibits an excellent high-temperature resistance, which makes AVG still show the excellent strength of 437.66 MPa and toughness of 11.16 MPa⋅m 1/2 after heat treatment at 1500 °C for 100 h and they are respective 2.51 times and 3.18 times higher than Al 2 O 3 in the same condition. This work provides a new thought for the preparation of high-strength, ultra-tough and high-temperature mechanical stable ceramics. • In-suit vertical graphene (VG) with active atomic edges formed a crosslinked and interlocked nanointerface after sintering. • The strength and toughness of VG-enhanced alumina ceramics (AVG) respective reached 444.16 MPa and 13.79 MPa⋅m 1/2 . • AVG maintained the strength of 437.66 MPa and toughness of 11.16 MPa⋅m 1/2 after heat treating for 100 h at 1500 °C.