Oxidation-resistant and rapid Cu sintering in an air atmosphere via the synergistic strategy of sustained release reduction and in-situ surface nanostructuring
Source abstract
Abstract
• Demonstration of oxidation-resistant Cu sintering in ambient air. • Oxidation resistance mechanism via sustained-release reduction is elucidated. • Rapid sintering of submicron Cu enabled by in-situ surface nanostructuring. • High shear strength of 38.1 MPa achieved after sintering at 250°C for 5 min.
Source: openalex_inverted_index · Quality: baseline
Research context
OpenAlex topics: Nanomaterials and Printing Technologies · nanoparticles nucleation surface interactions · Nanoporous metals and alloys
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (42)
Show source-provided references
1. Wang · IEEE Trans. Power. Electron. · 2024 · 39 · 1254510.1109/TPEL.2024.3401011 ↗
2. Murayama · Ceram. Int. · 2018 · 44 · 352310.1016/j.ceramint.2017.11.140 ↗
3. Chen · J. Alloy. Compd. · 2021 · 866
4. Wen · J. Mater. Res. Technol. · 2024 · 33 · 912310.1016/j.jmrt.2024.11.241 ↗
5. Zuo · Acta Mater. · 2022 · 23610.1016/j.actamat.2022.118135 ↗
6. Gao · J. Electron. Mater. · 2017 · 46 · 457510.1007/s11664-017-5464-2 ↗
7. Wang · Mater. Charact. · 2024 · 209
8. Xiao · J. Mater. Sci.: Mater. Electron. · 2022 · 33 · 12604
9. Yamagiwa · J. Mater. Sci.: Mater. Electron. · 2021 · 32 · 19031
10. Wang · J. Mater. Process. Technol. · 2024 · 332
11. Liu · Scr. Mater. · 2016 · 120 · 8010.1016/j.scriptamat.2016.04.018 ↗
12. Zhang · Appl. Phys. A-Mater. Sci. Process. · 2021 · 127 · 1
13. Gao · Mater. Des. · 2018 · 160 · 126510.1016/j.matdes.2018.11.003 ↗
14. Cao · Mater. Des. · 2025 · 256
15. Shi · J. Mater. Chem. C · 2026 · 14 · 469610.1039/D5TC04491J ↗
16. Wang · ACS Appl. Mater. Interfaces · 2024 · 16 · 167510.1021/acsami.3c12389 ↗
17. Verma · Int. J. Pharm. Investig. · 2022 · 12 · 19910.5530/ijpi.2022.2.35 ↗
18. Li · J. Mater. Sci. Technol. · 2023 · 139 · 21010.1016/j.jmst.2022.08.031 ↗
19. Guo · Acta Mater. · 2025 · 28210.1016/j.actamat.2024.120471 ↗
20. Park · J. Electron. Mater. · 2022 · 51 · 385110.1007/s11664-022-09634-3 ↗
21. Yang · J. Mater. Res. Technol. · 2024 · 28 · 435010.1016/j.jmrt.2024.01.026 ↗
22. Kaur · J. Mater. Sci.: Mater. Electron. · 2022 · 33 · 16154
23. Lenglet · Mater. Res. Bull. · 1995 · 30 · 39310.1016/0025-5408(95)00025-9 ↗
24. Golonka · Biol. Pharm. Bull. · 2017 · 40 · 119910.1248/bpb.b16-00967 ↗
25. Jingyan · J. Pharm. Biomed. Anal. · 2013 · 77 · 11610.1016/j.jpba.2013.01.018 ↗
26. Ikegawa · ACS ES T Water · 2024 · 4 · 516910.1021/acsestwater.4c00775 ↗
27. Liu · J. Taiwan. Inst. Chem. Eng. · 2021 · 125 · 39410.1016/j.jtice.2021.06.026 ↗
28. Payne · Polym. Degrad. Stab. · 2021 · 18310.1016/j.polymdegradstab.2020.109388 ↗
29. Wang · ACS Appl. Mater. Interfaces · 2024 · 16 · 167510.1021/acsami.3c12389 ↗
30. Wenande · Clin. Exp. Allergy · 2016 · 46 · 90710.1111/cea.12760 ↗
31. Winiarski · Ultramicroscopy · 2021 · 22610.1016/j.ultramic.2021.113315 ↗
32. Tiamiyu · Nat. Mater. · 2022 · 21 · 78610.1038/s41563-022-01250-0 ↗
33. Johnson · J. Appl. Phys. · 1969 · 40 · 19210.1063/1.1657030 ↗
34. Hu · Mater. Today Commun. · 2023 · 34
35. German · 2014
36. Van Swygenhoven · Phys. Rev. B · 2000 · 62 · 83110.1103/PhysRevB.62.831 ↗
37. Oh-Ishi · Acta Mater. · 2013 · 61 · 348210.1016/j.actamat.2013.02.042 ↗
38. Takrori · Appl. Surf. Sci. · 2017 · 401 · 6510.1016/j.apsusc.2016.12.208 ↗
39. Highly Reliable Cu Particles Sinter Joining for Die-attach of Next Generation Power Devices
40. Jia · ACS Appl. Mater. Interfaces · 2020 · 12 · 1674310.1021/acsami.9b20731 ↗
41. Ide · Mater. Trans. · 2006 · 47 · 21110.2320/matertrans.47.211 ↗
42. Alekseeva · Mater. Sci. Eng. B · 2024 · 29910.1016/j.mseb.2023.116984 ↗