Microstructural Characteristics and Tensile Behavior of Vacuum-Fusion-Welded Joints in 2507 Duplex Stainless-Steel Pipes

To address the performance deficiencies in welded joints in 2507 duplex stainless-steel pipes under demanding service conditions such as deep-sea operation, this study investigates drawn 2507 duplex stainless-steel pipes. Vacuum-fusion welding coupled with ER2507 wire filling is employed to fabricate the joints. The joint microstructure and tensile behavior are systematically analyzed using microstructural characterization techniques (electron backscatter diffraction and transmission electron microscopy) and uniaxial tensile testing. The results indicate that the joint exhibits a graded microstructure along the welding direction: base metal-heat affected zone-weld metal. The austenite phase fraction in the fusion zone decreases to 27.6%. The joint achieves an ultimate tensile strength of 833.3 MPa and a total elongation of close to 23%, demonstrating an excellent combination of strength and ductility. During tensile deformation, the ferrite and austenite phases undergo coordinated deformation. Strain is distributed relatively uniformly at low strain levels but localized preferentially within the fusion zone at high strain levels. Fractographic analyses reveal a ductile fracture mode. This research provides theoretical support and technical reference for optimizing welding processes and assessing the service safety of 2507 duplex stainless-steel pipes in deep-sea pipeline-engineering applications.