Optimizing Substrate Bias to Enhance the Microstructure and Wear Resistance of AlCrMoN Coatings via AIP

In this work, arc ion plating (AIP) was employed to deposit AlCrMoN coatings on cemented carbide substrates, and the effects of substrate bias voltages (−80 V, −100 V, −120 V, and −140 V) on the microstructures, mechanical properties, and tribological behaviors of the coatings were investigated. The results showed that all AlCrMoN coatings exhibited a single-phase face-centered cubic (FCC) structure with columnar crystal growth and excellent adhesion to the substrate. As the negative bias voltage increased, the grain size of the coatings first decreased and then increased, while the hardness and elastic modulus showed a trend of first increasing and then decreasing, with the maximum hardness reaching 36.2 ± 1.33 GPa. Room-temperature ball-on-disk wear tests revealed that all four coatings demonstrated favorable wear resistance. The coating deposited at −100 V exhibited the lowest average friction coefficient of 0.47 ± 0.02 and wear rate ((3.27 ± 0.10) × 10−8 mm3/(N∙m)), featuring a smooth wear track with minimal oxide debris. During the steady-state wear stage, the dominant wear mechanisms of the AlCrMoN coatings were identified as oxidative wear combined with abrasive wear.