The adhesion strength and residual stress of colloidal-sol gel derived β-Tricalcium-Phosphate/Fluoridated-Hydroxyapatite biphasic coatings

Abstract β-tricalcium phosphate (β-TCP) powders are embedded in a fluoridated hydroxyapatite (FHA) matrix to form β-TCP-FHA composites via colloidal-sol gel method. This composite layer is deposited on top of a FHA layer to form a β-TCP-FHA/FHA biphasic coating. The effect of the nanosized powder on the residual stress is characterized through the X-ray diffraction peak shift. The powder incorporation increases the residual stress, while a large amount of β-TCP (Ca powder /Ca sol ratio is higher than 1/2) results in less gel shrinkage that partially compensates the mismatch of thermal expansion coefficient and thus the residual stress. Despite the elevated residual stress as more powders are embedded, the coating adhesion strength remains virtually constant: around 430 mN–500 mN in scanning scratch test.