Properties of Ni–Zn ferrite thin films deposited using spray pyrolysis

Abstract Nanocrystalline, homogeneous spinel Ni 1 − x Zn x Fe 2 O 4 thin films were deposited on glass substrates by using spray pyrolysis of metal nitrate aqueous solutions. The thickness of deposited films was below 500 nm, but crystallite size was under 30 nm. It has been shown that the DC resistivity, dielectric loss and optical band gap of deposited films are influenced by the zinc content. High DC resistivity and low dielectric losses of thin Ni 1 − x Zn x Fe 2 O 4 films are explained by mixed n-p conductivity and nanograin structure of spray pyrolysis deposited coatings which are changing with the ratio of Ni/Zn.