Structural, optical and magnetic properties of Zn1−xMnxO micro-rod arrays synthesized by spray pyrolysis method

Abstract Undoped and Mn-doped ZnO micro-rod arrays were fabricated by the spray pyrolysis method on glass substrates. X-ray diffraction and scanning electron microscopy showed that these micro-rod arrays had a polycrystalline wurtzite structure and high c -axis preferred orientation. Photoluminescence studies at 10 K show that the increase of manganese content leads to a relative decrease in deep level band intensity with respect to undoped ZnO. Magnetic measurements indicated that undoped ZnO was diamagnetic in nature whereas Mn-doped ZnO samples exhibited ferromagnetic behavior at room temperature, which is possibly related to the substitution of Mn ions (Mn 2 + ) for Zn ions in the ZnO lattice.