Chemical vapor deposition of amorphous ruthenium–phosphorus alloy films

Abstract Chemical vapor deposition growth of amorphous ruthenium–phosphorus films on SiO 2 containing ∼ 15% phosphorus is reported. cis -Ruthenium(II)dihydridotetrakis-(trimethylphosphine), cis -RuH 2 (PMe 3 ) 4 (Me = CH 3 ) was used at growth temperatures ranging from 525 to 575 K. Both Ru and P are zero-valent. The films are metastable, becoming increasingly more polycrystalline upon annealing to 775 and 975 K. Surface studies illustrate that demethylation is quite efficient near 560 K. Precursor adsorption at 135 K or 210 K and heating reveal the precursor undergoes a complex decomposition process in which the hydride and trimethylphosphine ligands are lost at temperatures as low at 280 K. Phosphorus and its manner of incorporation appear responsible for the amorphous-like character. Molecular dynamics simulations are presented to suggest the local structure in the films and the causes for phosphorus stabilizing the amorphous phase.