Growth and characterization of Bi2Se3 thin films by pulsed laser deposition using alloy target

Bi(2)Se(3) thin films were deposited on the (100) oriented Si substrates by pulsed laser deposition technique at different substrate temperatures (room temperature -400 degrees C). The effects of the substrate temperature on the structural and electrical properties of the Bi(2)Se(3) films were studied. The film prepared at room temperature showed a very poor polycrystalline structure with the mainly orthorhombic phase. The crystallinity of the films was improved by heating the substrate during the deposition and the crystal phase of the film changed to the rhombohedral phase as the substrate temperature was higher than 200 degrees C. The stoichiometry of the films and the chemical state of Bi and Se elements in the films were studied by fitting the Se 3d and the Bi 4d5/2 peaks of the X-ray photoelectron spectra. The hexagonal structure was seen clearly for the film prepared at the substrate temperature of 400 degrees C. The surface roughness of the film increased as the substrate temperature was increased. The electrical resistivity of the film decreased from 1 x 10(-3) to 3 x 10(-4) Omega cm as the substrate temperature was increased from room temperature to 400 degrees C. (C) 2011 Elsevier B.V. All rights reserved.