Fabrication of TiO2 nanotube arrays by electrochemical anodization in an NH4F/H3PO4 electrolyte

Abstract Highly ordered TiO 2 nanotube arrays were fabricated by electrochemical anodization of titanium in an NH 4 F/H 3 PO 4 electrolyte. A TiO 2 crystal phase was identified by X-ray diffraction, and the morphology, length and pore diameter of the TiO 2 nanotube arrays were determined by field-emission scanning electron microscopy (FE-SEM). The anodization parameters including the rate of magnetic stirring, F − concentration, calcination temperature, anodization voltage and anodization time were investigated in detail. The results show that the as-prepared TiO 2 nanotube arrays possessed good uniformity, a well-aligned morphology with a length of 750 nm and an average pore diameter of 62 nm at a 150 rpm rate of magnetic stirring for 120 min at 20 V in an electrolyte mixture of 0.2 M H 3 PO 4 and 0.3 M NH 4 F with a 500 °C calcination to obtain 100% anatase phase. The adsorption of N-719 dye at different tube lengths was determined by UV-vis analysis and found to increase with increasing tube length. We also discuss the formation mechanism of the TiO 2 nanotube arrays. The findings indicate that the formation of the TiO 2 nanotube arrays proceeds by the combined action of the electrochemical etching and chemical dissolution.