Effect of CdCl2 annealing treatment on thin CdS films prepared by chemical bath deposition

Abstract In order to study the CdS recrystallization mechanism, a comparative study was carried out on thin films prepared by chemical bath deposition. The CdS films were annealed in air with or without a CdCl 2 coating layer. In-situ Raman spectra obtained during the annealing showed that both the air- and the CdCl 2 -annealing did not cause rearrangement of the neighboring atoms in the CdS clusters below ~ 300 °C. CdS thin film was partially oxidated to CdO and CdSO 4 on the cluster surface when annealed in air. The oxides and the sulfur stoichiometric deficiency prevented the clusters to coalesce at higher temperatures. Coating thin CdS film with a thin CdCl 2 layer protected it from oxidation during annealing in air and promoted formation of Cl S and V Cd point defects in CdS. The anti-oxidation was attributed to the incorporation of a significant amount of Cl into CdS to form the Cl S , which prevented the oxygen in-diffusion and chemical bonding during the annealing. The anti-oxidation at the CdS nano-crystalline surface and the point defects formed in the CdS promoted coalescence of the neighboring clusters without the need of long-range redistribution of the atoms. Large CdS grains with good crystalline quality formed through recrystallization during the CdCl 2 heat treatment, which provided the solid basis for the subsequent CdTe growth and high efficient CdS/CdTe solar cell fabrication.