Transparent p-AgCoO2/n-ZnO diode heterojunction fabricated by pulsed laser deposition

Abstract Transparent diode heterojunction on ITO coated glass substrates was fabricated using p-type AgCoO 2 and n-type ZnO films by pulsed laser deposition (PLD). The PLD of AgCoO 2 thin films was carried out using the pelletized sintered target of AgCoO 2 powder, which was synthesized in-house by the hydrothermal process. The band gap of these thin films was found to be ∼ 3.89 eV and they had transmission of ∼ 55% in the visible spectral region. Although Hall measurements could only indicate mixed carrier type conduction but thermoelectric power measurements of Seebeck coefficient confirmed the p-type conductivity of the grown AgCoO 2 films. The PLD grown ZnO films showed a band gap of ∼ 3.28 eV, an average optical transmission of ∼ 85% and n-type carrier density of ∼ 4.6 × 10 19 cm − 3 . The junction between p-AgCoO 2 and n-ZnO was found to be rectifying. The ratio of forward current to the reverse current was about 7 at 1.5 V. The diode ideality factor was much greater than 2.