Optical, electrical and thermal studies on (As2Se3)3−x(As2Te3)x glasses

Abstract Optical properties and conductivity of glassy (As2Se3)3−x(As2Te3)x were studied for 0 ≤ x ≤ 3. The films of the above mentioned compound were prepared by thermal evaporation with thickness of about 250 nm. The optical-absorption edge is described and calculated using the non-direct transition model and the optical band gap is found to be in the range of 0.92 to 1.84 eV. While, the width of the band gap tail exhibits opposite behaviour and is found to be in the range of 0.157 to 0.061 eV, this behaviour is believed to be associated with cohesive energy and average coordination number. The conductivity measurement on the thin films is reported in the temperature range from 280 to 190 K. The conduction that occurs in this low-temperature range is due to variable range hopping in the band tails of localized states, which is in reasonable agreement with Mott's condition of variable range hopping conduction. Some parameters such as coordination number, molar volume and theoretical glass transition temperature were calculated and discussed in the light of the topological bonding structure.