Atomic layer deposition and characterization of biocompatible hydroxyapatite thin films

Abstract Atomic layer deposition (ALD) was used to produce hydroxyapatite from Ca(thd) 2 (thd = 2,2,6,6-tetramethyl-3,5-heptanedionato) and (CH 3 O) 3 PO onto Si(100) and Corning (0211). Film crystallinity, stoichiometry, possible impurities and surface morphology were determined. The as-deposited films contained significant amounts of carbonate impurities however, annealing at moist N 2 flow reduced the carbonate content even at 400 °C. The as-deposited Ca–P–O films were amorphous but rapid thermal annealing promoted the formation of the hydroxyapatite phase. Mouse MC 3T3-E1 cells were used for the cell culture experiments. According to the bioactivity studies cell proliferation was enhanced on as-deposited ALD-grown Ca–P–O films and greatly enhanced on films annealed at 500 °C in comparison with reference cells on borosilicate glass or cell culture polystyrene.