Intrinsic microcrystalline silicon prepared by hot-wire chemical vapour deposition for thin film solar cells

Microcrystalline silicon (μc-Si:H) prepared by hot-wire chemical vapour deposition (HWCVD) at low substrate temperature T s and low deposition pressure exhibits excellent material quality and performance in solar cells. Prepared at T s below 250 °C, μc-Si:H has very low spin densities, low optical absorption below the band gap, high photosensitivities, high hydrogen content and a compact structure, as evidenced by the low oxygen content and the weak 2100 cm -1 IR absorption mode. Similar to PECVD material, solar cells prepared with HWCVD i-layers show increasing open circuit voltages V oc with increasing silane concentration. The best performance is achieved near the transition to amorphous growth, and such solar cells exhibit very high V oc up to 600 mV. The structural analysis by Raman spectroscopy, X-ray diffraction (XRD) and transmission electron microscopy (TEM) shows considerable amorphous volume fractions in the cells with high V oc . Raman spectra show a continuously increasing amorphous peak with increasing V oc . Crystalline fractions X C ranging from 50% for the highest V oc to 95% for the lowest V oc were obtained by XRD. XRD-measurements with different incident beam angles, TEM images and electron diffraction patterns indicate a homogeneous distribution of the amorphous material across the i-layer. Nearly no light induced degradation was observed in the cell with the highest X C , but solar cells with high amorphous volume fractions exhibit up to 10% degradation of the cell efficiency.