Unequal {110} Facets: The Potential Role of Intraparticle Heterogeneity and Facet Termination in Photoelectrochemical Activity of Single BiVO₄ Particles

BiVO 4 photoanodes are promising for solar water splitting, with photogenerated electrons and holes preferentially reacting at top {010} and lateral {110} facets, respectively. However, the mechanisms driving this facet-dependent reactivity remain unclear. Here, we investigate facet-dependent photocurrent and material heterogeneity using correlative scanning photoelectrochemical microscopy (SPCM), electron beam induced current (EBIC) mapping, and mid-IR scattering scanning near-field optical microscopy (s-SNOM). SPCM measurements of 62 BiVO 4 particles confirmed higher photocurrents at lateral {110} facets compared to top {010} facets, but unexpectedly revealed variations in photocurrent among lateral facets within the same particle. Variations in lateral facet surface termination could explain the intraparticle-level reactivity heterogeneity, consistent with theoretical predictions. Nano-FTIR spectroscopy and Raman microspectroscopy indicated significant materials chemistry heterogeneity within individual particles and facets that could be attributed to variations in lattice vibration distortions that enhance the overlap between Bi 6s and O 2p orbitals. The increased orbital overlap is significant as it potentially increases hole mobility in the valence band and potentially explains the lateral facet-dependent charge separation efficiency observed in photocurrent maps. Facet-dependent electrical and EBIC measurements showed no space charge regions at interfacet junctions or metal-BiVO 4 contacts under vacuum, suggesting that photogenerated holes beneath top {010} facets are unlikely to transport to lateral {110} facets to drive water/sulfite oxidation. These findings indicate the potential influence of distinct bulk properties and surface termination chemistries across different particles and facets, highlighting the importance of carefully controlling defects and surface chemistry during sample growth to optimize photocatalytic performance.