Periodic Titania Nanostructures Using Block Copolymer Templates

The deposition of periodic titania nanostructures, templated by a polystyrene-block-poly(4-vinylpyridine) (PS-b-P4VP) block copolymer, is reported. When cast as a thin film (30-50 nm thick), the PS-b-P4VP forms a morphology that consists of P4VP cylinders that are orientated perpendicular to the substrate. The P4VP phase was lightly cross-linked by exposing the film to diiodobutane. When the block copolymer film was exposed to the sol-gel titania precursor, titanium(IV) bis(ammonium lactate) dihydroxide (TALH), titania was formed in the P4VP phase. The resulting titania structures were identical in size to the P4VP cylinders and only formed (under the deposition conditions used in this study) when the block copolymer film was present on the substrate, thus providing evidence that the block copolymer indeed acts as a template. The process works for both silicon and indium tin oxide substrates.