INFLUENCE OF THE CaO CONTENT IN GLASS ON THE SINTERABILITY AND PROPERTIES OF A GLASS/Al₂O₃ COMPOSITE FOR LTCC APPLICATIONS
Source abstract
Abstract
2 O 3 -Al 2 O 3 -SiO 2 glass, sinterability, flexural strength
Only a short abstract or summary was supplied by the source.
Source: openalex_inverted_index · Quality: short
Research context
OpenAlex topics: Microwave Dielectric Ceramics Synthesis · Electrical and Thermal Properties of Materials · Ferroelectric and Piezoelectric Materials
SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.
References (40)
Show source-provided references
1. 10.1109/MAP.2015.241466810.1109/MAP.2015.2414668 ↗
2. 10.1179/174328008X27752410.1179/174328008X277524 ↗
3. 10.1111/j.1744-7402.2005.02052.x10.1111/j.1744-7402.2005.02052.x ↗
4. 10.1016/j.jeurceramsoc.2018.03.05310.1016/j.jeurceramsoc.2018.03.053 ↗
5. 10.1007/s10854-016-4690-310.1007/s10854-016-4690-3 ↗
6. 10.1007/s10854-020-04293-810.1007/s10854-020-04293-8 ↗
7. 10.1179/1743280415Y.000000000710.1179/1743280415Y.0000000007 ↗
8. 10.1016/j.ceramint.2019.02.16810.1016/j.ceramint.2019.02.168 ↗
9. 10.1155/2012/5210.1155/2012/52 ↗
10. 10.1007/s10854-015-3728-210.1007/s10854-015-3728-2 ↗
11. 10.4028/www.scientific.net/KEM.697.25710.4028/www.scientific.net/KEM.697.257 ↗
12. 10.1016/j.ceramint.2019.05.07710.1016/j.ceramint.2019.05.077 ↗
13. 10.1007/s12540-013-3004-z10.1007/s12540-013-3004-z ↗
14. 10.1111/jace.1427110.1111/jace.14271 ↗
15. 10.1016/j.ceramint.2018.12.20110.1016/j.ceramint.2018.12.201 ↗
16. 10.1007/s10854-020-04718-410.1007/s10854-020-04718-4 ↗
17. 10.1007/s10854-018-8929-z10.1007/s10854-018-8929-z ↗
18. 10.1016/j.jeurceramsoc.2020.09.04610.1016/j.jeurceramsoc.2020.09.046 ↗
19. 10.1002/9780470310519.ch510.1002/9780470310519.ch5 ↗
20. 10.1007/s10853-012-6318-110.1007/s10853-012-6318-1 ↗
21. 10.1007/s10854-020-03961-z10.1007/s10854-020-03961-z ↗
22. 10.1016/j.ceramint.2020.12.14010.1016/j.ceramint.2020.12.140 ↗
23. 10.1142/s021797921950070x10.1142/s021797921950070x ↗
24. 10.1515/ntrev-2019-004110.1515/ntrev-2019-0041 ↗
25. 10.1016/j.jallcom.2008.11.16310.1016/j.jallcom.2008.11.163 ↗
26. 10.1111/j.1744-7402.2009.02425.x10.1111/j.1744-7402.2009.02425.x ↗
27. 10.1016/j.matchemphys.2017.05.02810.1016/j.matchemphys.2017.05.028 ↗
28. 10.1016/j.vibspec.2013.05.01510.1016/j.vibspec.2013.05.015 ↗
29. 10.1016/j.ijrmhm.2018.09.01510.1016/j.ijrmhm.2018.09.015 ↗
30. 10.1016/j.matchemphys.2019.12221210.1016/j.matchemphys.2019.122212 ↗
31. 10.1016/j.jeurceramsoc.2019.07.03210.1016/j.jeurceramsoc.2019.07.032 ↗
32. 10.1016/j.jallcom.2011.04.12910.1016/j.jallcom.2011.04.129 ↗
33. 10.1016/j.ceramint.2018.03.14010.1016/j.ceramint.2018.03.140 ↗
34. 10.1016/j.ceramint.2021.11.25910.1016/j.ceramint.2021.11.259 ↗
35. 10.1021/j100605a00910.1021/j100605a009 ↗
36. 10.1111/j.1551-2916.2005.00497.x10.1111/j.1551-2916.2005.00497.x ↗
37. 10.4028/www.scientific.net/KEM.803.8810.4028/www.scientific.net/KEM.803.88 ↗
38. 10.1016/j.jallcom.2019.05.14110.1016/j.jallcom.2019.05.141 ↗
39. 10.1016/j.ceramint.2010.01.00510.1016/j.ceramint.2010.01.005 ↗
40. 10.1111/j.1551-2916.2005.00578.x10.1111/j.1551-2916.2005.00578.x ↗